hot rolled 310s 310 stainless steel coil

hot rolled 310s 310 stainless steel coil

310S high temperature, 321 corrosion is quite good in the case of high temperatures or 310S is more suitable for the maximum temperature can reach 1200 °C, oxidation resistance, corrosion resistance, acid and alkali, high temperature performance is much better than 321.

Hot Rolled 310s 310 Stainless Steel Coil Suppliers | Manufacturer | Exporter
Huaxiao Capacity about 310s Hot rolled stainless steel coil,310s HRC
310s Stainless Steel Coil SpecificationASTM A240 / ASME SA240
AISI 310s Stainless Steel Coil Manufacturing ProcessHot Rolled (HR)
310s Stainless Steel Coil Thickness1.2mm – 10mm, etc.
310s Stainless Steel Coil Width600 MM/1250 MM / 1500 MM / 2000 MM / 04 Feet / 05 Feet and Custom Cut Width as Per Requirement
310s Stainless Steel Coil Length2400 MM / 2420 MM / 6000 MM / 08 Feet / 10 Feet / Coil Cut and Custom Cut Length as Per Requirement
310s Stainless Steel Coil CoatingPVC coating Normal / Laser, Film: 100 micrometers, Color: black/white, etc.
310s Stainless Coil Surface FinishNO.1, 1D, 2D, #1, hot rolled finished, black, Anneal and pickling, mill finish
310s Stainless Coil Shipment & TransportationTrain Partial Load, Full Load, By Sea – Break-bulk Conventional Vessel / FCL (Full Container Load) / LCL (Less Container Load) / 20 Feet Container / 40 Feet Container / 45 Feet Container / High Cube Container / Open Top Container, By Air – Freighter Civil Passenger and Cargo Planes
310s Stainless Steel Coil Value Added ServicesGas Cutting / CNC Plasma Cutting / Profiling / Rolling / Bending / Coil Metal Fabrication / Drill / Punch / Machining / Sand Blasting / Shot Blasting / Heat Treatment
MillTISCO, Baosteel, JUSCO, etc.
Max Coil25MT and Custom as Per Requirement

If you need to know 310 stainless steel prices, please free to contact 310 stainless steel suppliers Huaxiao.

Grade Specifications for Stainless Steel 310 / 310S Coils
STANDARDWERKSTOFF NR.UNSJISBS GOSTAFNOREN
SS 3101.4841S31000SUS 310310S2420Ch25N20S2X15CrNi25-20
SS 310S1.4845 S31008SUS 310S310S1620Ch23N18X8CrNi25-21

310/310s Same grade from the different standard, 310 Stainless Steel

1.4841 S31000 SUS310S 1.4845 S31008 S31008S 06Cr25Ni20 0Cr25Ni20 high temperature stainless steel

S31008 Chemical component ASTM A240 :
CSiMnCrNiSPMoN
≤ 0.08≤1.5≤ 2.016.00~18.0010.0~14.00≤0.03≤0.0452.0-3.0≤0.1

S31008 mechanical property ASTM A240:
Tensile Strength> 515 Mpa
Yield Strength>205 Mpa
Elongation (%)> 40%
Hardness< HRB95

PHYSICAL PROPERTIES:
Density (lb./ in^2) @ RT0.29
Modulus of Elasticity in Tension (psi x 10^6)29.0
Specific Heat (BTU/o F/lb.)32 to 212 oF0.12
Thermal Conductivity (BTU/hr/ft^2/ft)212oF8.0
932oF10.8
Mean Coefficient of Thermal Expansion (in. x 10^-6 per o F)68 to 212oF8.8
68 to 932oF9.5
68 to 1832oF10.5
Electrical Resistivity (micro ohms – cm)at 70oF30.7
Oxidation Resistance – Continuous Service(oF)2000
Simple description about 310s/310 stainless steel

High temperature resistant stainless steel, also known as 310S (0Cr25Ni20) stainless steel 310 stainless steel, is austenitic chromium-nickel stainless steel, has good oxidation resistance, corrosion resistance, because a higher percentage of chromium and nickel, so that has much better creep strength, Can continue to work at high temperatures, with good high-temperature resistance.

Due to the high content of nickel (Ni) and chromium (Cr), it has good oxidation resistance, corrosion resistance, acid and alkali resistance, high-temperature resistance, high-temperature resistant steel is specially used in the production of electric furnace tubes and other occasions, carbon in austenitic stainless steel After the content, due to its solid solution strengthening effect,

the strength of the austenitic stainless steel is added to the chromium, nickel-based molybdenum, tungsten, tantalum, and titanium, due to its face-centered cubic structure.

Therefore, it has high strength and creeps strength at high temperatures.

Comparison about 310s and 321

310S stainless steel high temperature, 321 stainless steel corrosion is quite good in the case of high temperatures or 310S is more suitable for the maximum temperature can reach 1200 °C, oxidation resistance, corrosion resistance, acid and alkali, high-temperature performance is much better than 321

Comparison about 310s and 316L stainless steel
Corrosion resistance

316L is molybdenum-containing stainless steel that can be used between 15% and 85% sulfuric acid. (But the material properties will drop in a high-temperature environment)

The 310S can be used between 15% and 50% sulfuric acid. (Due to its high heat resistance in high-temperature environments, material properties will not decrease

Heat resistance, Wear resistance

Because 310S has a higher melting point than 316L, it is more wearable than 316L in high-temperature, high-speed friction environments.