Mainly used for materials other than DDQ applications. This 304 ddq stainless steel material is characterized by relatively low elongation (≧45%), relatively high hardness (≦180HB), and internal grain size grade of 8.0~9.0. Compared with DDQ material, its deep drawing performance is relatively poor.
304DQ/DDQ cold rolled stainless steel coil
304 ddq stainless steel, 304 DQDDQ cold rolled stainless steel coil(0.2mm-8mm)
Huaxiao Capacity about 304 DQDDQ cold rolled stainless steel coil, 304 DQ DDQ CRC
Thickness: 0.2mm – 8.0mm
Width: 600mm – 2000mm, the narrowed products pls check in strip products
Max coil weight: 25MT
Coil ID: 508mm,610mm
304 DQ DDQ Same grade from different country standard
SUS304DQ SUS304DDQ S30408DQ 06Cr19Ni10DQ 0Cr18Ni9DQ S30400DQ
304DQ DDQ Chemical component ASTM A240:
C：≤0.08 ，Si ：≤0.75 Mn ：≤2.0 ，Cr ：18.0～20.0 ，Ni ：8.0～10.5， S ：≤0.03 ，P ：≤0.045 N≤0.1
304DQ DDQ mechanical property ASTM A240:
Tensile strength: > 515 Mpa
Yield Strength: >205 Mpa
Elongation (%): > 53%
Hardness: < HRB92
Description about DQ, DDQ and normal material
304 ddq stainless steel material is widely be used as all kinds of stainless steel kitchenware,
DDQ (deep drawing quality) material refers to the material used for deep drawing (redrawing), which is what we call soft material. The main characteristic of this material is its high elongation (≧53%), hardness Low (≦170%), internal grain grade between 7.0~8.0, excellent deep drawing performance. Many companies that produce thermos and pots generally have higher processing ratios (BLANKING SIZE/product diameter), and their processing ratios are 3.0, 1.96, 2.13, and 1.98, respectively.
SUS304 ddq stainless steel material is mainly used for these higher processing ratios of the product, of course, the processing ratio of more than 2.0 products generally have to undergo a few passes to complete the stretch. If the raw material extension is not reachable, the product can easily produce cracks and pull-throughs when processing deep-drawing products, affecting the qualification rate of finished products, and of course, increase the cost of the manufacturers.
General materials: Mainly used for materials other than DDQ applications. This 304 ddq stainless steel material is characterized by relatively low elongation (≧45%), relatively high hardness (≦180HB), and internal grain size grade of 8.0~9.0. Compared with DDQ material, its deep drawing performance is relatively poor. It is mainly used for products that can be obtained without stretching, like spoons, spoons, forks, electrical appliances, and steel pipes for a type of tableware. However, it has an advantage over DDQ materials in that BQ properties are relatively good, mainly due to its slightly higher hardness.
What is the difference between 304 and 304DDQ stainless steel?
Compared with 304, the CR content of 304DQ is increased by half to one, and the polishing is better. Compared with 304, the content of 304DDQ has not changed. The content of NI is increased by half to one, and the deep drawing and deep drawing are better. “Soft material” but poor polishing performance. . 304DDQ stainless steel uses a special process to increase the chromium content of 304 stainless steel by 2 points (304 steel plate is 18/8, 304 DDQ is 18/10), which means that the content of nickel (Ni) in 304 stainless steel is 18%, and chromium ( The content of Cr) is 8%; the content of nickel (Ni) in the improved 304DDQ stainless steel is 18%, and the content of chromium (Cr) is 10%; the steel plate has high brightness, no discoloration and beautiful appearance, but also has the best Good ductility, toughness and corrosion resistance.