310/310s cold rolled stainless steel sheets

Home/Stainless Steel Sheet/Plate/Stainless Steel Sheets(0.05mm-8mm)/310/310s cold rolled stainless steel sheets

310/310s cold rolled stainless steel sheets

Application of 310s/310 stainless steel sheet
Commonly used in the manufacture of steam boilers, steam turbines, industrial furnaces and aviation, petrochemical and other industrial parts of the parts at high temperature.

Sample of 310/310s Cold Rolled Stainless Steel Sheets, 310 stainless steel sheet
Huaxiao Capacity about 310s cold rolled stainless steel sheets

Thickness: 0.2mm – 3.0mm

Width: 300mm – 1500mm, the narrowed products pls check in strip products

Length: 1000mm-6000mm

Finish: 2B

310/310s Same grade from different standard

1.4841 S31000 SUS310S 1.4845 S31008 S31008S 06Cr25Ni20 0Cr25Ni20 high temperature stainless steel

S31008 Chemical component ASTM A240 :

C:≤ 0.08 ,Si: ≤1.5  Mn: ≤ 2.0 ,Cr:16.00~18.00 ,Ni:10.0~14.00,S :≤0.03 ,

P :≤0.045 Mo: 2.0-3.0 , N≤0.1

S31008 mechanical property ASTM A240:
  • Tensile strength : > 515 Mpa
  • Yield Strength : >205 Mpa
  • Elongation (%): > 40%
  • Hardness < HRB95
General Description of 310/310S

310S stainless steel is austenitic chromium-nickel stainless steel, with good oxidation resistance, resistance Corrosive, because of the higher percentage of chromium and nickel, so much better creep strength, continuous operation at high temperatures, with good temperature resistance. Due to the high nickel (Ni), chromium (Cr) content, with good resistance to oxidation, corrosion resistance, acid and alkali, high temperature performance, high temperature resistant steel pipe used in the manufacture of electric furnace tubes and other occasions, austenitic stainless steel to increase carbon Content, due to its solid solution strengthening to enhance the strength of austenitic stainless steel chemical composition based on chromium, nickel-based addition of molybdenum, tungsten, niobium and titanium and other elements, due to its organization of face-centered cubic structure, Thus at high temperatures have high strength and creep strength. Melting point 1470°C, 800°C began to soften, allowable stress continued to decrease.

Application of 310s/310 stainless steel sheet

Commonly used in the manufacture of steam boilers, steam turbines, industrial furnaces and aviation, petrochemical and other industrial parts of the parts at high temperature.

Cold rolled and hot rolled to 310/310s