Stainless Steel Coil
Stainless Steel Sheets (0.05mm-8mm)
Stainelss Steel Plate (1.2mm-200mm)
Stainless Steel Strip (0.05mm-10mm)
Decorative Stainless Steel Sheets
Stainless Steel Bar & Wire
Updates
Advantages and Applications of Colored Stainless Steel Sheets
Research Says Cooking Oil Can Make Stainless Steel Surfaces Antibacterial
Canada'S First Anti Dumping Review Of China'S Steel Pile Pipe Industry Affirmed Final Damage
The European Union Carries Out Protective Tariffs On Steel
Thailand Strengthens Control Over Chinese Steel Products That Are Transported To The United States V

301 Cold Rolled Stainless Steel Coil

Huaxiao Capacity about 301 cold rolled stainless steel coil, 301 CRC

Thickness: 0.2mm - 3.0mm
Width: 600mm - 1500mm, the narrowed products pls check in strip products
Max coil weight: 10MT
Coil ID: 508mm, 610mm
Finish: 2B, 2D
  • Advantage

301 Same grade from different mill standard

1.4310  SUS301  06Cr17Ni7

301 Chemical component  ASTM A240 :

C:≤0.15 ,Si :≤1.0 Mn:2.0 ,Cr:16~18.00 ,Ni:6.0~8.0, S :≤0.03 ,P :≤0.045 , N≤0.1

301 mechanical property

Tensile strength :  > 515 Mpa
Yield Strength :  >205 Mpa
Elongation (%):  > 40%
Hardness: < HRB95

Description about 301 stainless steel


301 (17Cr-7Ni-carbon) material: Compared with 304 steel, Cr, Ni content is small, tensile strength and hardness increase during cold processing, non-magnetic, but magnetic after cold processing. Uses: trains, aircraft, conveyors, vehicles, bolts, springs, screens.

The 301 stainless steel is a metastable austenitic stainless steel and has a fully austenitic structure under full solution conditions. Among the stainless steels, 301 is the steel that is most easily deformed by cold deformation. Through cold deformation processing, the strength and hardness of the steel can be improved, and sufficient plasticity and toughness can be retained. In addition, the steel has good rust resistance under atmospheric conditions. However, the corrosion resistance of the reducing media is poor, and the corrosion resistance of chemical media such as acid and alkali salts is poor. Therefore, it is not recommended for use in corrosive environments. 301 is mainly used in cold working conditions to withstand higher loads, but also to reduce equipment weight and rust-free equipment components. In addition, this steel is susceptible to work hardening when it is impacted by external forces, absorbing more impact energy and providing more reliable safety protection for equipment and personnel.

301 GB grade is 1Cr17Ni7304 GB code 0Cr18Ni9, so compare 301 to 304 steel, due to lower Cr and Ni content, so the corrosion resistance is greatly reduced. After cold rolling can improve the tensile strength. 301 was originally no magnetic, but After cold rolling, it will have magnetic properties.
Leave a Message Email Us

we will contact you within 24 hours.

Related Products
  • 410/410s Cold Rolled Stainless Steel Sheets (0.2mm-8mm)

    410/410s Cold Rolled Stainless Steel Sheets (0.2mm-8mm)

    August 10, 2018Huaxiao Capacity about 410 410s cold rolled stainless steel sheets, 410 410s CRCThickness: 0.2mm - 8.0mmWidth: 100mm - 2000mmLength: 500mm – 6000mmPallet weight: 25MTFinish: 2B,2D410 Similar grade fr...view
  • 410 410s Cold Rolled Stainless Steel Coil

    410 410s Cold Rolled Stainless Steel Coil

    April 22, 2018410 Similar grade from different country standardS41000 SUS410 1.4006 1.4000 06Cr13 S11306 0Cr13410 Chemical Component :C:≤0.08-0.15 ,Si :≤1.0 Mn :≤1.0 , S :≤0.03 ,P :≤0.040, Cr :11.5~13.5 ,Ni :0.75 Max,410 Mechanical Property :Tensile stren...view
  • Polished Stainless Steel Plate

    Polished Stainless Steel Plate

    August 10, 2018Huaxiao Capacity about Polished stainless steel plateFinish: No.3, No.4, No.5, SB, Color coating, #3, #4, #8, Hair Line(HL)Film: PVC, PE, PI, Laser PVC, 20um-120umThickness: 4.0mm - 100mmWidth: 300mm ...view
  • TEL:+86-21-54725826
  • FAX:+86-21-54717930
  • EMAIL:export@huaxiao-ss.com
  • ADDRESS:Room 458, Building 8-9, NO.1500 South Lianhua Road, Shanghai, China.